Potassium Titanyl Phosphate (KTiOPO4 or KTP) is widely used in both commercial and military lasers including laboratory and medical systems, range-finders, lidar, optical communication and industrial ..
|
Crystal Structure
|
Orthorhombic, space group Pna21,point group mm2
|
|
Lattice Parameter
|
a=6.404A, b=10.616A, c=12.814A, Z=8
|
|
Melting Point
|
About 1172°C
|
|
Mohs Hardness
|
5
|
|
Density
|
3.01 g/cm3
|
|
Thermal Conductivity Coefficient
|
13W/m/K
|
|
Thermal Expansion Coefficient
|
ax=11x10-6/0C, ay=9x10-6/0C, az=0.6x10-6/0C
|
|
Transparency Range
|
350~4500nm
|
|
SHG Phase Matchable Range
|
497 ~ 1800nm (Type II)
|
|
Thermal-optic Coefficients (/°C)
|
dnx/dT=1.1X10-5
dny/dT=1.3X10-5 dnz/dT=1.6X10-5 |
|
Absorption Coefficients
|
<0.1%/cm at 1064nm <1%/cm at 532nm
|
|
For Type II SHG of a Nd:YAG laser at 1064nm
|
Temperature Acceptance: 24°C-cm
Spectral Acceptance: 0.56nm-cm Angular Acceptance: 14.2mrad-cm (φ);55.3mrad-cm (q) Walk-off Angle: 0.55° |
|
NLO Coefficients
|
deff(II)≈(d24 - d15)sin2fsin2q - (d15sin2f + d24cos2f)sinq
|
|
Non-vanished NLO Susceptibilities
|
d31=6.5 pm/V d24=7.6 pm/V
d32= 5 pm/V d15=6.1 pm/V d33=13.7 pm/V |
|
Sellmeier Equations
|
nx2=3.0065+0.03901/(l 2-0.04251)-0.01327l 2
ny2=3.0333+0.04154/(l 2-0.04547)-0.01408l 2 nz2=3.3134+0.05694/(l 2-0.05658)-0.01682l 2 |
|
Specification
|
Standard
|
High Precision
|
|
Dimensions
|
Size: Up to 20x20mm2
Thickness: 0.01mm to 25mm
|
|
|
Dimension Tolerance
|
+/-0.1mm
|
+/-0.01mm
|
| Wavefront Distortion |
λ/8
|
λ/8
|
|
Flatness
|
λ/10
|
λ/10
|
|
Surface Quality
|
10/5
|
10/5
|
|
Orientation
|
+/-0.3°
|
+/-0.1°
|
|
Parallelism
|
20’’
|
10’’
|
|
Specificationg
|
|
|
Type
|
AR Coaing or P Coating
|
|
Damage Threshold
|
>500MW/cm2
|